Thehydrogenoxidationreaction(HOR)inalkalineelectrolytesexhibitsmarkedlyslowerkineticsthanthatinacidic electrolytes.Thisposesacriticalchallengeforalkalineexchangemembranefuelcells(AEMFCs).Theslowerkineticsinalkaline electrolytesisoftenattributedtothemoresluggishVolmerstep(hydrogendesorption).IthasbeenshownthatthealkalineHOR activityonthePtsurfacecanbeconsiderablyenhancedbythepresenceofoxophilictransitionmetals(TMs)andsurface-adsorbed hydroxylgroupsonTMs(TM−OHad),althoughtheexactroleofTM−OHadremainsatopicofactivedebates.Herein,usingsingle- atomRh-tailoredPtnanowiresasamodelsystem,wedemonstratethathydroxylgroupsadsorbedontheRhsites(Rh−OHad)can profoundly reorganize the Pt surface water structure to deliver a record-setting alkaline HOR performance. In situ surface characterizations,togetherwiththeoreticalstudies,revealthatsurfaceRh−OHadcouldpromotetheoxygen-downwater(H2O↓)that favorsmorehydrogenbondwithPtsurfaceadsorbedhydrogen(H2O↓···Had-Pt)thanthehydrogen-downwater(OH2↓).TheH2O↓ furtherservesasthebridgetofacilitatetheformationofanenergeticallyfavorablesix-membered-ringtransitionstructurewith neighboringPt−Had andRh−OHad,thusreducingtheVolmerstepactivationenergyandboostingHORkinetics. 

Abstract Iron‐nitrogen‐carbon (Fe‐N‐C) single‐atom catalysts are promising sustainable alternatives to the costly and scarce platinum (Pt) to catalyze the oxygen reduction reactions (ORR) at the cathode of proton exchange membrane fuel cells (PEMFCs). However, Fe‐N‐C cathodes for PEMFC are made thicker than Pt/C ones, in order to compensate for the lower intrinsic ORR activity and site density of Fe‐N‐C materials. The thick electrodes are bound with mass transport issues that limit their performance at high current densities, especially in H₂/air PEMFCs. Practical Fe‐N‐C electrodes must combine high intrinsic ORR activity, high site density, and fast mass transport. Herein, it has achieved an improved combination of these properties with a Fe‐N‐C catalyst prepared via a two‐step synthesis approach, constructing first a porous zinc‐nitrogen‐carbon (Zn‐N‐C) substrate, followed by transmetallating Zn by Fe via chemical vapor deposition. A cathode comprising this Fe‐N‐C catalyst has exhibited a maximum power density of 0.53 W cm⁻²in H₂/air PEMFC at 80 °C. The improved power density is associated with the hierarchical porosity of the Zn‐N‐C substrate of this work, which is achieved by epitaxial growth of ZIF‐8 onto g‐C₃N₄, leading to a micro‐mesoporous substrate.